White fused alumina electrically fused in arc furnace with high grade processed alumina as raw material. It has higher hardness and slight lower toughness comparing with brown fused alumina. It is also characterized by its high purity, ability of self-sharpening, better cutting, less heat emit, higher efficiency.
White fused aluminum oxide becomes the first choice for the sandblasting technics, meanwhile, it is also the ideal material for abrasive and workpiece cleaning, and polishing.
Comparing with brown fused alumina, white aluminum oxide is also characterized by its high purity, acid and alkali resistance, good thermal stability. It’s the high grade refractory materials.
| Typical Chemical composition | |
| AL2O3 | 99.3%min |
| SiO2 | 0.06% |
| Na2O | 0.3%max |
| Fe2O3 | 0.05%max |
| CaO | 0.04%max |
| MgO | 0.01%max |
| K2O | 0.02#max |
| Typical physical properties | |
| Hardness: | Mohs:9.0 |
| Maximum service temperature: | 1900 ℃ |
| Melting Point: | 2250 ℃ |
| Specific Gravity: | 3.95g/cm3 |
| Volume density | 3.6g/cm3 |
| Bulk density(LPD): | 1.75-1.95 g/cm3 |
| Color: | White |
| Particle shape: | Angular |
| Available size: | |
| F8# F10# F12# F14# F16# F20# F22# F24# F30# F36# F46# F54# F60# F70# F80# F90# F100# F120# F150# F180# F220# | |
| Grit | 1 | 2 | 3 | 3 and 4 | 5 | Q5（≤） | ||||
| W1 (um) | Q1 | W2(um) | Q2（≤） | W3(um) | Q3（≥） | W4(um) | Q3+Q（≥） | W5(um) | ||
| F8 | 4000 | 0 | 2800 | 20% | 2360 | 45% | 2000 | 70% | 1700 | 3% |
| F10 | 3350 | 0 | 2360 | 20% | 2000 | 45% | 1700 | 70% | 1400 | 3% |
| F12 | 2800 | 0 | 2000 | 20% | 1700 | 45% | 1400 | 70% | 1180 | 3% |
| F14 | 2360 | 0 | 1700 | 20% | 1400 | 45% | 1180 | 70% | 1000 | 3% |
| F16 | 2000 | 0 | 1400 | 20% | 1180 | 45% | 1000 | 70% | 850 | 3% |
| F20 | 1700 | 0 | 1180 | 20% | 1000 | 45% | 850 | 65% | 710 | 3% |
| F24 | 1180 | 0 | 850 | 25% | 710 | 45% | 600 | 65% | 500 | 3% |
| F30 | 1000 | 0 | 710 | 25% | 600 | 45% | 500 | 65% | 425 | 3% |
| F36 | 850 | 0 | 600 | 25% | 500 | 45% | 425 | 65% | 355 | 3% |
| F40 | 710 | 0 | 500 | 30% | 425 | 40% | 355 | 65% | 300 | 3% |
| F46 | 600 | 0 | 425 | 30% | 355 | 40% | 300 | 65% | 250 | 3% |
| F54 | 500 | 0 | 355 | 30% | 300 | 40% | 250 | 65% | 212 | 3% |
| F60 | 425 | 0 | 300 | 30% | 250 | 40% | 212 | 65% | 180 | 3% |
| F70 | 355 | 0 | 250 | 25% | 212 | 40% | 180 | 65% | 150 | 3% |
| F80 | 300 | 0 | 212 | 25% | 180 | 40% | 150 | 65% | 125 | 3% |
| F90 | 250 | 0 | 180 | 20% | 150 | 40% | 125 | 65% | 106 | 3% |
| F100 | 212 | 0 | 150 | 20% | 125 | 40% | 106 | 65% | 90 | 3% |
| F120 | 180 | 0 | 125 | 20% | 106 | 40% | 90 | 65% | 75 | 3% |
| F150 | 150 | 0 | 106 | 15% | 90 | 40% | 75 | 65% | 63 | 3% |
| F180 | 125 | 0 | 90 | 15% | 75 | * | 63 | 40% | 53 | * |
| F220 | 106 | 0 | 75 | 15% | 63 | * | 53 | 40% | 45 | * |