white fused alumina is produced by fusing pure alumina in electric arc furnaces at the Boksitogorsk Alumina Refinery. Due to its ultra-high strength, white fused alumina is used for producing abrasive tools, and because of its resistance to high temperatures and low thermal and electrical conductivity, is in the production of ceramic and refractory products.

Physical Properties Hardness: micro 21600-22600kg/mm3 Hardness: Mohs 9.0 min Specific Gravity 3.95-3.97g/cm3 Bulk Density 1.65-2.05g/cm3 Particle Shape Blocky, Sharp Color white Chemical compositions Al2O3 99.40min SiO2 0.15max Na2O 0.28max Fe2O3 0.06max CaO 0.03max Applications of White Fused Alumina Abrasives for Wear Resistant Ceramic Tile —Bonded abrasive tool —Coated abrasive tool —Reusable abrasive —Grinding,lapping & polishing medium —Raw material for

WA – White Fused Alumina WA is a fused white alumina abrasive powder produced by crushing fused alumina and sorting the particles into a uniform size. The resulting compound has the following characteristics: An α‑type corundum crystal configuration At least a 96.0% pure aluminum oxide (Al2O3) composition A hardness nearly equal to silicon carbide A closely

—Description The WFA is the main raw material for the production of unshaped and shaped refractory materials. Commonly used in ladle castables, iron runner materials, refractory gunning mix materials and other monolithic refractory products; For the shaped refractory materials, it is mainly used in the high-quality raw materials of corundum brick, corundum mullite, refining steel

Physical Properties Hardness: micro 21600-22600kg/mm3 Hardness: Mohs 9.0 min Specific Gravity 3.95-3.97g/cm3 Bulk Density 1.65-2.05g/cm3 Particle Shape Blocky, Sharp Color white Chemical compositions Al2O3 99.40min SiO2 0.15max Na2O 0.28max Fe2O3 0.06max CaO 0.03max Applications of White Fused Alumina WA/WFA White Aluminum Oxide: —Bonded abrasive tool —Coated abrasive tool —Reusable abrasive —Grinding,lapping & polishing medium —Raw material for foundry ,coating

White aluminum oxide was made from the high quality alumina by melting above 2200℃ in the electric arc furnace and cooling.   White aluminum oxide is white with the main crystal phase alpha-Al2O3.   White aluminum oxide produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability