Fused white Alox with 99.3% Al2O3

Typical Chemical composition AL2O3 99.3%min SiO2 0.06% Na2O 0.3%max Fe2O3 0.05%max CaO 0.04%max MgO 0.01%max K2O 0.02#max Typical physical properties Hardness: Mohs:9.0 Maximum service temperature: 1900 ℃ Melting Point: 2250 ℃ Specific Gravity: 3.95g/cm3 Volume density 3.6g/cm3 Bulk density(LPD): 1.75-1.95 g/cm3 Color: White Particle shape: Angular Available size: FEPA F230 F240 F280 F320 F360 F400

Read More »

White Aluminum Oxide Grit Specifications

Physical and Chemical Composition   Physical Properties Hardness: micro 21600-22600kg/mm3 Hardness: Mohs 9.0 min Specific Gravity 3.95-3.97g/cm3 Bulk Density 1.65-2.05g/cm3 Particle Shape Blocky, Sharp Color white Chemical compositions Al2O3 99.40min SiO2 0.15max Na2O 0.28max Fe2O3 0.06max CaO 0.03max Typical Size   Fraction sand or powder Grit designation Passing rate % 0-1mm 90 1-3mm 90 3-5mm

Read More »

White Electrofused Alumina – White Alumina Powder

White aluminum oxide is white with the main crystal phase alpha-Al2O3,it is made from the high quality alumina by melting above 2200℃ in the electric arc furnace and cooling.   White aluminum oxide produced in titling electric arc furnace has the advantage of high bulk density and low porosity and the volume stability and thermal shock resistance can

Read More »

White Aluminum Oxide Micron Powder

AL2O3 alumina polishing powder is a white abrasive made from industrial alumina powder (Al2O3) with a content of over 98% and a small amount of iron oxide and silicon oxide. It is a white abrasive which is melted at high temperature. Its hardness is slightly higher than that of brown corundum and its toughness is slightly

Read More »

White Fused Alumina Grit for Abrasives

Applications Mainly used in abrasive industry, such as bonded abrasives, coated abrasives. Bonded abrasives Coated abrasives Gunning material Refractory raw materials Packaging 25 kg bags on pallet up to 1 ton 1 ton loose in big bag As requirements Technical Composition: FEPA Average grain size(µm) FEPA Average grain size(µm) FEPA Average grain size(µm) FEPA Average

Read More »

White Aluminum Oxide (WHITE ALOX) –Blasting Abrasive

 White Aluminum Oxide is raw material characterized with high hardness, yet friable with high purity, chemical stability, a high melting point, and large crystal size. It is used in many applications including grinding and cut off wheels, coated abrasives, laminates, coatings, blasting, lapping and polishing. Physical Data: Color: White Shape: Blocky with sharp edges Mohs Hardness: